The quality of epoxy floor paint needs to be judged after construction. We can judge by the following performance indicators: 1. Adhesion: Adhesion refers to the ability of the epoxy floor paint film and the surface of the coated substrate or the combination of coatings, also known as adhesion. Adhesion is an important technical index and a prerequisite for a series of properties of paint film. The paint film with good adhesion is durable. Lacquer film with poor adhesion is easy to crack and fall off, and can not be used.2、表干時(shí)間

2. Watch drying time

指環(huán)氧地坪漆施工在地面上，表層已經(jīng)固化，手碰觸不會(huì)留下痕跡，但底層還沒(méi)有固化所需要的時(shí)間。

Epoxy floor paint construction on the ground, the surface has been solidified, hand touch will not leave traces, but the underlying has not yet solidified the time required.3、實(shí)干時(shí)間

3. Working time

指環(huán)氧地坪漆施工的那層環(huán)氧地坪漆從底層到表層都固化完全所需要的時(shí)間。一般為24小時(shí)以?xún)?nèi)。

Refers to the time required for the floor paint to be solidified from the bottom to the surface. Usually within 24 hours.4、漆膜光澤度

4. Gloss of paint film

物體表面被光照射時(shí)，光線(xiàn)朝一定方向反射的性能即為光澤。地坪漆漆膜光澤是其外觀(guān)質(zhì)量的重要指標(biāo)之一，關(guān)系到漆膜的使用性能，常用光澤度測(cè)定儀檢測(cè)，當(dāng)漆膜出現(xiàn)微縫、下陷和老化時(shí)，就開(kāi)始失去光澤。影響地坪漆漆膜光澤的因素很多，主要有涂料品種與性能、基材性質(zhì)、涂飾方法、涂飾工藝等。

When the surface of an object is illuminated by light, the performance of light reflecting in a certain direction is gloss. The gloss of floor paint film is one of the important indicators of its appearance quality, which is related to the performance of the paint film. The gloss tester is often used to detect the gloss. When there are slits, subsidence and aging of the paint film, it begins to lose its gloss. There are many factors affecting the gloss of the floor paint film, such as the variety and performance of the paint, the properties of the base material, the finishing methods and the finishing process.5、拉伸強(qiáng)度

5. Tensile Strength

指地坪漆漆膜在外力拉伸的情況下，單位面上上不發(fā)生斷裂或塑變所能承受的力。一般環(huán)氧砂漿地坪漆拉升強(qiáng)度要求不小于70Mpa。

It refers to the force that the floor paint film can bear without breaking or plastic deformation on the unit surface when it is stretched by external force. Generally, the tensile strength of epoxy mortar floor paint is not less than 70 Mpa.6、硬度

6. Hardness

硬度是地坪漆漆膜抵抗諸如碰撞、壓陷、擦劃等機(jī)械力作用的能力。 漆膜硬度高，則其表面機(jī)械強(qiáng)度高，耐磨性好，能耐磕碰擦劃等。但是，漆膜硬度并非越高越好，過(guò)硬的漆膜容易脆裂，影響附著力，抗沖擊強(qiáng)度也低。

Hardness is the resistance of floor paint film to mechanical forces such as collision, indentation and scratch. The film has high hardness, high surface mechanical strength, good wear resistance and resistance to bump, scratch and so on. However, the hardness of the film is not the higher the better, the hard film is easy to crack, affect the adhesion, impact strength is also low.7、抗折強(qiáng)度

7. Flexural Strength

指地坪漆在外力下不彎曲折斷單位面積所承受的力。環(huán)氧砂漿地坪漆一般要求不低于6Mpa。

Refers to the force that the floor paint bears per unit area without bending or breaking under external force. Epoxy mortar floor paint generally requires no less than 6 Mpa.8、抗沖擊性

8. Impact Resistance

指地坪漆在被體以較高的速度沖擊時(shí)所能承受的力。一般要求1KG的物體從50cm高的物體下跌落，地坪漆漆膜無(wú)損。

Refers to the force that floor paint can withstand when the quilt is impacted at a higher speed. It is generally required that a 1KG object fall from a 50cm high object and the floor paint film is undamaged.9、耐磨性

9. Wear resistance

耐磨性表示地坪漆漆膜對(duì)摩擦作用的抵抗能力。 一般要求用重750G的物體，在失重的情況下，旋轉(zhuǎn)摩擦500圈，地坪漆前后重量不超過(guò)0.02克。

Wear resistance indicates the resistance of the floor paint film to friction. It is generally required to use objects weighing 750G. In the case of weightlessness, the weight of floor paint should not exceed 0.02g before and after 500 cycles of rotational friction.10、耐熱性

10. Heat Resistance

地坪漆漆膜的耐熱性是指漆膜抵抗熱量的能力。耐熱性差的漆膜遇熱可能出現(xiàn)變色、失光、印痕、鼓泡、起皺、開(kāi)裂等現(xiàn)象。

The heat resistance of the floor paint film refers to the heat resistance of the paint film. The poor heat resistance paint film may appear discoloration, loss of gloss, imprint, bubbling, wrinkling, cracking and other phenomena when heated.